SS-7039 - Product Detail - Arconic Spectrochemical Reference Materials - Arconic Portal

SS-7039

$975.00

SS-7039, 7XXX Type Certified Reference Material for Wrought Alloy Analysis

Alloy Designation

7039

Größe

64mm diameter x 25mm thickness (Size is Approximate)

Im Lager

Si

0.15

Fe

0.2

Cu

0.08

Mn

0.25

Mg

3.0

Cr

0.2

Ni

0.02

Zn

4.0

Ti

0.05

Ag

<0.0010

As

<0.0010

B

<0.0010

Be

0.001

Bi

<0.0010

Ca

<0.0005

Cd

<0.0010

Co

<0.0010

Ga

0.02

Li

<0.0005

Na

<0.0005

P

<0.0010

Pb

<0.0030

Sb

<0.0010

Sc

<0.0010

Sn

<0.0010

Sr

<0.0010

V

0.01

Zr

<0.0030

T

Weight Percent (%)

Estimated Uncertainty

Cd

0.0000

0.0002

Mn

0.256

0.004

B

0.0001

0.0002

Ce

Mo

In

Ag

0.0000

0.0002

Co

0.0002

0.0002

Cr

0.197

0.003

P

(0.0001)

As

0.0000

0.0002

Cu

0.0867

0.0009

Pb

0.0012

0.0004

Na

0.0000

0.0002

S

Zn

4.01

0.06

Ti

0.0481

0.0007

Weight Percent (%)

Estimated Uncertainty

La

V

0.0093

0.0004

Zr

0.0011

0.0004

Ni

0.0197

0.0009

Li

0.00001

0.00005

Fe

0.209

0.003

Hg

Be

0.0013

0.0004

Bi

0.0001

0.0002

Sb

(0.0000)

Sc

0.0000

0.0002

Si

0.140

0.006

Ga

0.0193

0.0004

Mg

3.00

0.05

Sn

0.0000

0.0002

Ca

0.0001

0.0002

Sr

0.0001

0.0002

Associated Accreditation

-

Registered to ISO 9001:2015 by BSI

Certified Date: 2025-11-14

U

Weight Percent (%)

Estimated Uncertainty

Cd

0.0000

0.0002

Mn

0.256

0.004

B

0.0001

0.0002

Ce

Mo

In

Ag

0.0000

0.0002

Co

0.0002

0.0002

Cr

0.197

0.003

P

(0.0001)

As

0.0000

0.0002

Cu

0.0867

0.0009

Pb

0.0012

0.0004

Na

0.0000

0.0002

S

Zn

4.01

0.06

Ti

0.0481

0.0007

Weight Percent (%)

Estimated Uncertainty

La

V

0.0093

0.0004

Zr

0.0011

0.0004

Ni

0.0197

0.0009

Li

0.00001

0.00005

Fe

0.209

0.003

Hg

Be

0.0013

0.0004

Bi

0.0001

0.0002

Sb

(0.0000)

Sc

0.0000

0.0002

Si

0.140

0.006

Ga

0.0193

0.0004

Mg

3.00

0.05

Sn

0.0000

0.0002

Ca

0.0001

0.0002

Sr

0.0001

0.0002

Associated Accreditation

-

Registered to ISO 9001:2015 by BSI

Certified Date: 2025-11-14