LI-2397 - Product Detail - Arconic Spectrochemical Reference Materials - Arconic Portal

LI-2397

$1,275.00

LI-2397, 2XXX Certified Reference Material for Aluminum Lithium Alloy Analysis

Alloy Designation

2397

Taille

65mm diameter x 25mm thickness (Size is Approximate)

En stock

Si

0.05

Fe

0.05

Cu

2.8

Mn

0.3

Mg

0.12

Cr

<0.0050

Ni

<0.0050

Zn

0.1

Ti

0.06

Ag

0.001

As

<0.0010

B

0.001

Be

<0.0005

Bi

<0.0010

Ca

5.0E-4

Cd

<0.0010

Co

<0.0010

Ga

<0.020

Li

1.4

Na

5.0E-4

P

<0.0010

Pb

5.0E-4

Sb

<0.0010

Sc

<0.0010

Sn

<0.0010

Sr

<0.0010

V

<0.020

Zr

0.12

A

Weight Percent (%)

Estimated Uncertainty

Cd

0.0000

0.0002

Mn

0.292

0.004

B

0.0002

0.0002

Ce

Mo

In

Ag

0.0028

0.0004

Co

0.0001

0.0002

Cr

0.0003

0.0002

P

(0.0000)

As

(0.0001)

Cu

2.72

0.04

Pb

0.0007

0.0002

Na

0.0002

0.0002

S

Zn

0.106

0.002

Ti

0.054

0.002

Weight Percent (%)

Estimated Uncertainty

La

V

0.0082

0.0006

Zr

0.123

0.002

Ni

0.0035

0.0005

Li

1.44

0.03

Fe

0.049

0.001

Hg

Be

0.00002

0.00005

Bi

0.0000

0.0002

Sb

(0.0000)

Sc

(0.0000)

Si

0.0508

0.0008

Ga

0.0108

0.0004

Mg

0.0970

0.0009

Sn

0.0003

0.0002

Ca

0.0003

0.0002

Sr

0.0000

0.0002

Associated Accreditation

-

Registered to ISO 9001:2015 by Bureau Veritas

Certified Date: 2017-09-18

B

Weight Percent (%)

Estimated Uncertainty

Cd

0.0000

0.0002

Mn

0.304

0.005

B

0.0002

0.0002

Ce

Mo

In

Ag

0.0028

0.0004

Co

0.0001

0.0002

Cr

0.0002

0.0002

P

(0.0000)

As

(0.0001)

Cu

2.72

0.04

Pb

0.0006

0.0002

Na

0.0002

0.0002

S

Zn

0.106

0.002

Ti

0.0547

0.0009

Weight Percent (%)

Estimated Uncertainty

La

V

0.0081

0.0006

Zr

0.123

0.002

Ni

0.0034

0.0004

Li

1.41

0.03

Fe

0.048

0.002

Hg

Be

0.00002

0.00005

Bi

0.0000

0.0002

Sb

(0.0001)

Sc

(0.0000)

Si

0.0507

0.0009

Ga

0.0106

0.0004

Mg

0.087

0.002

Sn

0.0002

0.0002

Ca

0.0003

0.0002

Sr

0.0000

0.0002

Associated Accreditation

-

Registered to ISO 9001:2015 by Bureau Veritas

Certified Date: 2017-09-18